JOHN TEK
NSSC 550 MATERIAL
-
TEST 01SALT SPRAY TEST REPORT
6,000-15,000 HRS MIN
-
TEST 02KESTERNICH TEST REPORT
OVER 100 CYCLE
MORE THAN 2,400 HRS -
TEST 03HARDNESS TEST REPORT
SURFACE HARDNESS:620-635 HV
CORE HARDNESS:559-563 HV
SGS REPORT DOWNLOAD
COMPARISON CHART
01 | METERIAL | John Tek #550 |
Bi-Metal |
C1022 |
|
02 |
SIZE |
#10 | #10 | #10 | |
03 |
TENSILE TEST |
161.9 kgf/mm2 | 70.7 kgf/mm2 | 132.4 kgf/mm2 | |
04 | SALT SPRAY TEST REPORT | 8,000-15,000 hours |
ZINC+WAXING | RUSPERT | ZINC |
24 HRS(5μ) 72 HRS(8μ) |
240~1,000 HRS | 24~48 HRS(5μ) 48~120 HRS(8μ) |
MORE JOHN TEK 550 PRODUCT
CORPORATE WITH NIPPON STEEL FOR THE SPECIAL MATERIAL NSSC550 (YUS550),SPENDING 18 YEARS TO DEVELOP IT.

rOOFING SCREW
JOHN TEK 550
YOU DON'T NEED TO WORRY ABOUT CHANGING IT OFTENLY, WHEN USING NSSC550 ROOFING SCREW. IT CAN PREVENT THE RUST FOR OVER 250 YEARS.